The raw materials of conductive devices must have both high conductivity and certain strength. 6101B aluminum alloy can be heat treated to strengthen,
Therefore, 6101B T6 Aluminum Tubular Busbar has good electrical conductivity and has been classified as a conductive material.
Material performance requirements of 6101B T6 Aluminum Tubular Busbar: yield strength ≥ 100 MPa, tensile strength ≥ 130 MPa, electrical conductivity ≥ 56% IACS.
Chemical Composition of 6101B T6 Aluminum Tubular Busbar
Al (minimum value): margin
Si: 0.30~0.7
Fe: ≤0.50
Cu: ≤0.10
Mn: ≤0.03
Mg: 0.35~0.8
Cr:≤0.03
Zn:≤0.10
B:≤0.06
Ti:—
Other elements not specified: each: ≤0.03; total: ≤0.10
The Application of 6101B T6 Aluminum Tubular Busbar
The best process for 6101B T6 Aluminum Tubular Busbar is 5% pre-stretching after quenching, and the artificial aging system is (260±3)℃×6h. At this time, the yield strength is 111.3MPa, the tensile strength is 149.3MPa, and the electrical conductivity is 56.90% LACS, the performance meets customer requirements, and is used to produce high-strength electrical bus bars.